Sintered
NdFeB |
Residual Induction Br(KGs) |
Coercive Force bHc (KOe) |
Intrinsic Coercive Force iHc (KOe) |
Maximum Energy Product
(BH)max (MGOe) |
Curie Temperature Tc (°C) |
Vickers Hardness Hv |
Working Temperature Tw (°C) |
TemperatureCoefficient (0-100 °C) (%/ °C) |
||||
|
N-27 N-30 N-33 N-35 N-38 N-40 N-43 N-45 N-48 N-27H N-30H N-33H N-35H N-38H N-40H N-42H N-27SH N-30SH N-33SH N-35SH N-38SH N-27UH N-30UH N-33UH N-28EH N-30EH |
Nom. 10.6 11.2 11.7 12.1 12.6 12.9 13.3 13.7 14.0 10.6 11.2 11.7 12.1 12.6 12.9 13.5 10.6 11.2 11.7 12.1 12.8 10.7 11.2 11.7 10.8 11.5 |
Min. 10.2 10.8 11.4 11.7 12.2 12.6 13.0 13.3 13.6 10.2 10.8 11.4 11.7 12.2 12.6 12.9 10.2 10.8 11.4 11.7 12.2 10.4 10.8 11.5 10.4 10.9 |
Nom. 9.8 10.5 11.0 11.5 11.5 11.0 11.0 11.0 11.0 10.0 10.7 11.0 11.5 12.0 12.0 12.9 10.2 11.0 11.0 11.5 12.1 10.4 10.6 11.0 10.2 11.2 |
Min. 9.3 9.8 10.3 10.8 10.8 10.5 10.5 10.5 10.5 9.3 10.0 10.3 10.8 11.5 11.5 11.5 9.6 10.2 10.3 10.8 11.4 10.0 10.1 10.3 9.8 10.0 |
>12.0 >12.0 >12.0 >12.0 >12.0 >12.0 >12.0 >12.0 >12.0 >17.0 >17.0 >17.0 >17.0 >17.0 >17.0 >17.0 >20.0 >20.0 >20.0 >20.0 >20.0 >26.0 >26.0 >26.0 >30.0 >30.0 |
Nom. 27 30 33 35 38 40 43 45 48 27 30 33 35 38 40 42 27 30 33 35 38 27 30 33 28 32 |
Min. 25 28 31 33 36 38 41 43 45 25 28 31 33 36 38 40 25 28 31 33 36 25 28 31 26 29 |
320-330 320-330 320-330 320-330 320-330 320-330 320-330 320-330 320-330 330-340 330-340 330-340 330-340 330-340 330-340 330-340 340-350 340-350 340-350 340-350 340-350 350-360 350-360 350-360 360-370 360-370 |
500-600 500-600 500-600 500-600 500-600 500-600 500-600 500-600 500-600 600-700 600-700 600-700 600-700 600-700 600-700 600-700 600-700 600-700 600-700 600-700 600-700 600-700 600-700 600-700 600-700 600-700 |
<80 <80 <80 <80 <80 <80 <80 <80 <80 <120 <120 <120 <120 <120 <120 <120 <150 <150 <150 <150 <150 <180 <180 <180 <200 <200 |
Br -0.11 -0.11 -0.11 -0.11 -0.11 -0.11 -0.11 -0.11 -0.11 -0.10 -0.10 -0.10 -0.10 -0.10 -0.10 -0.10 -0.10 -0.10 -0.10 -0.10 -0.10 -0.09 -0.09
-0.09 -0.09 -0.09 |
iHc -0.55 -0.55 -0.55 -0.55 -0.55 -0.55 -0.55 -0.55 -0.55 -0.51 -0.51 -0.51 -0.51 -0.51 -0.51 -0.51 -0.47 -0.47 -0.47 -0.47 -0.47 -0.43 -0.43 -0.43 -0.43 -0.43 |